Mirror aluminum alloy frame 6063

Introduction of mirror aluminum alloy frame 60636063 is an aluminum alloy with magnesium and silicon as alloying elements. It has generally good mechanical properties and is heat treatable and weldable. 6063 is the most common alloy used for aluminum extrusion. It allows the formation of complex shapes, has a very smooth surface...

Introduction of mirror aluminum alloy frame 6063

6063 is an aluminum alloy with magnesium and silicon as alloying elements. It has generally good mechanical properties and is heat treatable and weldable. 6063 is the most common alloy used for aluminum extrusion. It allows the formation of complex shapes, has a very smooth surface, is suitable for anodizing and is therefore ideal for architectural applications such as window frames, door frames, roofing and industrial profiles, framing aluminum profiles.

Performance of mirror aluminum alloy frame 6063

chemical composition:

Silicon Si: 0.20-0.6

Iron Fe: 0.35

Copper Cu: 0.10

Manganese Mn: 0.10

Magnesium Mg: 0.45-0.9

Chromium Cr: 0.10

Zinc Zn: 0.10

Titanium Ti: 0.10

Aluminum Al: Allowance

other:

Single: 0.05 Total: 0.15

Mechanical properties:

Tensile strength σb (MPa): ≥205

Elongation stress σp0.2 (MPa): ≥170

Elongation δ5 (%): ≥7

Note: Longitudinal mechanical properties of bar at room temperature

Sample size: diameter≤12.5

The advantages of using electrophoretic coating method in the processing of mirror aluminum alloy frame 6063

1. Easy to realize automatic production. Because the electrophoretic coating of the mirror aluminum alloy frame and the aluminum alloy line mirror frame is carried out in a water-based electrophoresis tank, similar to the anodizing and electrolytic coloring processes, the processing time is short, and it is easy to realize the assembly line operation of the entire process.
2. The coating film is uniform and dense. Due to the high penetrability of the electrophoretic coating of the aluminum profile, the aluminum alloy frame of the mirror with complex shape and the aluminum alloy line mirror frame can also obtain a uniform coating film, and the film thickness can be controlled by adjusting the power.
3. The utilization rate of paint is high. Due to the low viscosity, the aluminum material of the full-length mirror is less carried out, and the aluminum material of the electrophoretic full-length mirror can be washed with water.
4. Safety and environmental protection. Due to the water dilution of electrophoretic coatings, the solid content is low, and the solvent content is low. It is an environmentally friendly coating, and it avoids the danger of fire, and the health of workers is also guaranteed.
5. Mirror aluminum alloy frame the aluminum alloy line mirror frame has good coating quality. The acrylic resin is cured with amino resin, which ensures the high decoration and high corrosion resistance of the coating film. At the same time, because the resin is highly transparent, it effectively highlights the metallic texture of the aluminum profile, and can also obtain matt, sand, pearlescent light as required for other decorative effects.